Abstract
Highly layered structures are important to micro- and nanofabrication technologies for understanding and controlling surface structures through manipulation of chemical and physical interactions. The objective of this work was to develop a new approach to create micro- and nanopatterned surfaces using multilayer polymer films of commercially available and inexpensive polymers instead of inorganic substrates. As an example, linear low density polyethylene (LLDPE) and ethylene-co-acrylic acid copolymer (EAA) were used as alternating inert and reactive polymers, respectively. Thin cross-sections of the multilayer molded sheets were prepared by ultra-microtoming.
As a precursor to the multilayer work, surface modification of EAA was conducted to carefully control the chemical functionality on the surface by a variety of methods. Dansyl cadaverine and polyethylene glycol (PEG) derivatives were grafted on the surface of EAA film and in its subsurface region through formation of amides and esters, respectively. First, EAA film was activated with PCl5 and then the acid chloride was reacted with dansyl cadaverine or a PEG derivative. Moreover, two other reaction schemes were developed to covalently graft PEG chains on EAA surfaces. The schemes involved surface grafting of linker molecules l-lysine or polypropyleneamine dendrimer (AM64), with subsequent covalent bonding of PEG chains to the linker molecules. Combining the data from ATR-FTIR, XPS, and contact angle goniometry, it was found that the PEG chains were grafted on the surface of the EAA film and larger surface coverage was achieved when the dendrimer was used as intermediate layer.
Research was then conducted on the EAA-LLDPE multilayer cross-sectioned templates. Regionally confined chemical functionality was confirmed by grafting an amine-terminated biotin to the alternating layers of EAA. Subsequently, fluorescently labeled streptavidin selectively adsorbed on the biotin-modified EAA layers. As a further development, polyelectrolyte multilayers (PEM) were adsorbed on the nanopatterned surfaces to significant increase the areal density of reactive groups. Using PAH and PAA as the polyelectrolytes, the EAA nano-stripes were successfully modified by PEM films, forming a nanopatterned template with alternating hydrophilic and hydrophobic regions. This kind of nano-striped surface could serve as a template for many applications, including biomedical, separation, and electronics.
Recommended Citation
Zhang, Chun, "USING CROSS-SECTIONED MULTILAYER POLYMER FILM AND SURFACE MODIFICATION TO FORM CHEMICALLY PATTERNED SUBSTRATES " (2007). All Dissertations. 52.
https://open.clemson.edu/all_dissertations/52