Abstract

In this work, the hexagonal perovskite of targeted composition Ba5In2+xAl2Zr1-xO13 (x=0, 0.1, 0.2) was synthesized via a solid-state synthesis route to study the impact of oxygen vacancy concentration in layered hexagonal perovskites. Precursor oxides were mixed in stoichiometric proportions, calcined between 800-1200℃ and sintered at 1475℃. The sintered pellets were crushed into fine powders to investigate the chemistry and structure through X-ray diffraction, neutron diffraction, inductively coupled plasma mass spectrometry, and nuclear magnetic resonance. Dense pellets were used to study conductivity properties using electrochemical impedance spectroscopy.

The synthesis approach produced 100% phase pure material across a range of increasing indium content from 2.0 to 2.8, although not of the projected stoichiometries. Neutron diffraction and x-ray diffraction indicated fractional occupancy and site swapping of the indium and aluminum positions, which was not dependent on indium content and resulted in the newly detected O5 position.

From nuclear magnetic resonance, aluminum was proven to retain a strictly tetrahedral coordination. Additionally, the existence of four bulk protons was observed. Eight distinct oxygen signals were detected, likely the result of protonated and unprotonated forms of the various oxygen sites.

Impedance spectroscopy indicated a reduction of total conductivity at 600℃ from 10-4 to 10-5 S cm-1 from wet to dry air, with proton conduction consistent across the temperature range.

Share

COinS
 
 

To view the content in your browser, please download Adobe Reader or, alternately,
you may Download the file to your hard drive.

NOTE: The latest versions of Adobe Reader do not support viewing PDF files within Firefox on Mac OS and if you are using a modern (Intel) Mac, there is no official plugin for viewing PDF files within the browser window.